Our Tungsten Carbide (WC) Crucibles are engineered for the most demanding thermal and mechanical environments. Unlike standard graphite or ceramic crucibles, WC crucibles offer unparalleled hardness 90-92HRA and density 14.5-15.0 g/cm. These are specifically designed for applications where contamination must be minimized and the container must withstand aggressive abrasive forces or high-vacuum induction heating.
| Property | Value / Specification |
| Material Composition | 90-94% WC + 6-10% Co(Cobalt Binder) |
| Density | 14.5-15.0g/cm |
| Hardness | 90-92HRA |
| Melting Point | 2870WC Base |
| Transverse Rupture Strength | 2600MPa |
| Surface Roughness | < 0.4 μ Polished |
We offer a range of standard cylindrical and tapered geometries. Additionally, we provide OEM Customization for:
Wall thickness (for specific thermal gradients).
Integrated lids and pouring spouts.
Threaded bases for planetary ball mill integration.
| Diameter(mm) | Thickness(mm) | Height(mm) | Surface finish | inner surface finish | inner bottom finish |
| 30-50 | 2-10 | ≤200 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 50-100 | 3-15 | ≤300 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 100-150 | 3-15 | ≤350 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 150-200 | 5-20 | ≤400 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 200-300 | 8-25 | ≤500 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 300-400 | 8-30 | ≤600 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 400-450 | 8-30 | ≤650 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 450-600 | 8-35 | ≤800 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
Metallurgy: High-frequency induction melting of rare earth metals and alloys.
Laboratory Analysis: Used as milling jars or vessels for preparing high-purity geological or ceramic samples.
Crystal Growth: Specialized containers for growing synthetic crystals under high pressure/temperature.
Thin Film Deposition: Evaporation sources for vacuum coating processes.
Kí nìdí Yan Wa:
1. O le gba ohun elo pipe gẹgẹbi ibeere rẹ ni iye owo ti o kere julọ.
2. A tun nfun Awọn atunṣe, FOB, CFR, CIF, ati ẹnu-ọna si awọn owo ifijiṣẹ ẹnu-ọna. A daba pe ki o ṣe adehun fun gbigbe eyiti yoo jẹ ọrọ-aje pupọ.
3. Awọn ohun elo ti a pese jẹ iṣeduro patapata, lati ọtun lati ijẹrisi idanwo ohun elo aise si alaye iwọn ipari. (Awọn ijabọ yoo ṣafihan lori ibeere)
4. iṣeduro lati fun esi laarin awọn wakati 24 (nigbagbogbo ni wakati kanna)
5. O le gba awọn yiyan ọja iṣura, awọn ifijiṣẹ ọlọ pẹlu idinku akoko iṣelọpọ.
6. A ti wa ni kikun igbẹhin si awọn onibara wa. Ti ko ba ṣee ṣe lati pade awọn ibeere rẹ lẹhin idanwo gbogbo awọn aṣayan, a kii yoo tan ọ jẹ nipa ṣiṣe awọn ileri eke eyiti yoo ṣẹda awọn ibatan alabara to dara.
Ifihan ile-iṣẹ
PE WA
info@zztungsten.com