Our Tungsten Carbide (WC) Crucibles are engineered for the most demanding thermal and mechanical environments. Unlike standard graphite or ceramic crucibles, WC crucibles offer unparalleled hardness 90-92HRA and density 14.5-15.0 g/cm. These are specifically designed for applications where contamination must be minimized and the container must withstand aggressive abrasive forces or high-vacuum induction heating.
| Property | Value / Specification |
| Material Composition | 90-94% WC + 6-10% Co(Cobalt Binder) |
| Density | 14.5-15.0g/cm |
| Hardness | 90-92HRA |
| Melting Point | 2870WC Base |
| Transverse Rupture Strength | 2600MPa |
| Surface Roughness | < 0.4 μ Polished |
We offer a range of standard cylindrical and tapered geometries. Additionally, we provide OEM Customization for:
Wall thickness (for specific thermal gradients).
Integrated lids and pouring spouts.
Threaded bases for planetary ball mill integration.
| Diameter(mm) | Thickness(mm) | Height(mm) | Surface finish | inner surface finish | inner bottom finish |
| 30-50 | 2-10 | ≤200 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 50-100 | 3-15 | ≤300 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 100-150 | 3-15 | ≤350 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 150-200 | 5-20 | ≤400 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 200-300 | 8-25 | ≤500 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 300-400 | 8-30 | ≤600 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 400-450 | 8-30 | ≤650 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
| 450-600 | 8-35 | ≤800 | ≤Ra2.0 | ≤Ra2.4 | ≤Ra2.8 |
Metallurgy: High-frequency induction melting of rare earth metals and alloys.
Laboratory Analysis: Used as milling jars or vessels for preparing high-purity geological or ceramic samples.
Crystal Growth: Specialized containers for growing synthetic crystals under high pressure/temperature.
Thin Film Deposition: Evaporation sources for vacuum coating processes.
Aisea e Filifili ai Matou:
1. E mafai ona e mauaina le mea sili ona lelei e tusa ai ma lou manaʻoga i le tau maualalo.
2. Matou te ofoina atu foʻi Reworks, FOB, CFR, CIF, ma tau tuʻuina atu i le faitotoa. Matou te fautuaina oe e fai fefaʻatauaiga mo felauaiga o le a fai si taugofie.
3. O mea matou te tuʻuina atu e mafai ona faʻamaonia atoatoa, saʻo mai le tusi faʻataʻitaʻiga suʻega mataʻutia i le faʻamatalaga pito mulimuli.
4. faʻamautinoa e tuʻuina atu se tali i totonu ole 24 itula (masani ile itula lava e tasi)
5. E mafai ona e maua isi fa'atauga, fa'atauga fa'atau ma fa'aitiitia le taimi o gaosiga.
6. Matou te faʻamaoni atoatoa ia matou tagata faʻatau. Afai o le a le mafai ona ausia ou manaʻoga pe a uma ona suʻesuʻeina filifiliga uma, matou te le faʻasesēina oe e ala i le faia o folafolaga pepelo e faʻatupuina sootaga lelei tagata faʻatau.
Fa'aaliga falegaosimea
FAAFESOOTAI MATOU
info@zztungsten.com